LDPE Film Grade FC 243-55
CAS 9002-88-4
Generic registry number (not stated in the manufacturer TDS)
Low density polyethylene
- MFR – Melt mass-flow rate
- Typical: 2 g/10 min
- Density
- Typical: 922 kg/m³
- Tensile stress at break
- Typical: 22 / 16 MPa
- Tensile strain at break
- Typical: 230 / 560 %
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Appearance | Pellets | |
| MFR – Melt mass-flow rate | Typical: 2 g/10 min | ISO 1133-1 · g/10 min |
| Density | Typical: 922 kg/m³ | ISO 1183-2 · kg/m³ |
| Tensile stress at break | Typical: 22 / 16 MPa | ISO 527-1,3 |
| Tensile strain at break | Typical: 230 / 560 % | ISO 527-1,3 · % |
| Dart drop | Typical: 84 g | ISO 7765-1 method A |
| Haze | Typical: 10 % | ISO 14782 · % |
| Vicat softening temperature | Typical: 95 °C | ISO 306/A 120 · °C |
| Antiblock agent content | Typical: 800 ppm | Internal method · ppm |
| Slip agent content | Typical: 400 ppm | Internal method · ppm |
| Recommended film thickness | Typical: 0.02 – 0.06 mm | |
| Recommended processing temperature | Typical: 160 – 200 °C | °C |
Detailed application areas
Recommended for general purpose film; no guarantee. Users must test suitability and final article regulatory compliance (e.g. food contact). Suitable for conventional extrusion machines.
Packaging & storage
Packaging
25 kg PE bags; shrink/stretch-wrapped pallets, 1375 kg polymer. Road or rail silo transport also available.
Storage
Protect from UV and >40 °C. Humidity and temperature fluctuations may cause condensation; dry pellets before use if it occurs.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
LDPE Film Grade FC 243-55 (CAS 9002-88-4) is an industrial product in the thermoplastic polymers category. Typical specifications: Appearance: Pellets; MFR – Melt mass-flow rate: Typical: 2 g/10 min; Density: Typical: 922 kg/m³. KORKİMYA supplies LDPE Film Grade FC 243-55 in 25 kg PE bags; shrink/stretch-wrapped pallets, 1375 kg polymer. Road or rail silo transport also available..
Low density polyethylene
- CAS
- 9002-88-4
- TN-VED Code
- 3901 10
- Category
- Thermoplastic Polymers
Synonyms
Test Methods
ISO 1133-1 · ISO 1183-2 · ISO 527-1,3 · ISO 7765-1 method A · ISO 14782 · ISO 306/A 120 · Internal method
Key features
Why this product?
- Combustible; observe fire rules. Lift adhered bags without rotation first. [3] ISO 293 pressed specimens, ISO 291 room-temperature conditioning. [11] MD/TD film: 0.07 mm for MFR=0.3; 0.04 mm for MFR>0.3; blow-up ratio 2:1.
- [3] Values measured on standard pressed specimens (ISO 293) conditioned at room temperature (ISO 291).
- [11] Film properties in MD/TD: thickness 0.07 mm (MFR=0.3 g/10min) and 0.04 mm (MFR more than 0.3 g/10min), blow-up ratio 2:1.
- Films have excellent mechanical and optical properties; contains slip and antiblocking agents.
- REACH: Polymers are registration-exempt; monomers/relevant additives are registered, raw materials compliant.
- At publication, no identified SVHC >0.1%.
- Product compliance: see DDS.
- Recyclable by modern methods; keep in-house production waste clean for direct recycling.
- Heat-treated pallets are pooled for collection and reuse; they remain the pallet provider’s property.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com