LDPE Film Grade FC 03-03
CAS 9002-88-4
Generic registry number (not stated in the manufacturer TDS)
Additive-free LDPE with increased density
- MFR (190 °C, 2.16 kg)
- Typical: 0.3 g/10 min
- Density (23 °C) [1]
- Typical: 927 kg/m³
- Tensile stress at break (MD/TD) [6]
- Typical: 29 / 28 MPa
- Tensile strain at break (MD/TD) [6]
- Typical: 550 / 600 %
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| MFR (190 °C, 2.16 kg) | Typical: 0.3 g/10 min | ISO 1133-1 · °C |
| Density (23 °C) [1] | Typical: 927 kg/m³ | ISO 1183-1 · °C |
| Tensile stress at break (MD/TD) [6] | Typical: 29 / 28 MPa | ISO 527-1,3 |
| Tensile strain at break (MD/TD) [6] | Typical: 550 / 600 % | ISO 527-1,3 · % |
| Dart drop [6] | Typical: 150 g | ISO 7765-1 method A |
| Haze [6] | Typical: 5 % | ASTM D1003 · % |
| Vicat softening temperature [2] | Typical: 104 °C | ISO 306/A 50 · °C |
| Recommended film thickness | Typical: 0.06 – 0.22 mm | |
| Recommended processing temperature | Typical: 170 – 220 °C | °C |
Detailed application areas
Bags and pouches, blown films, shrink films, surface protection films and blow moulding products. Suitable for conventional extrusion machines. User must carry out tests for suitability and regulatory compliance.
Packaging & storage
Packaging
25 kg PE bags; shrink/stretch-wrapped pallet: 1375 kg polymer. Road or rail silo transport also available.
Storage
Protect from UV and temperatures above 40 °C. Dry before use if moisture condenses under high humidity and fluctuating temperatures.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
LDPE Film Grade FC 03-03 (CAS 9002-88-4) is an industrial product in the thermoplastic polymers category. Typical specifications: MFR (190 °C, 2.16 kg): Typical: 0.3 g/10 min; Density (23 °C) [1]: Typical: 927 kg/m³; Tensile stress at break (MD/TD) [6]: Typical: 29 / 28 MPa. KORKİMYA supplies LDPE Film Grade FC 03-03 in 25 kg PE bags; shrink/stretch-wrapped pallet: 1375 kg polymer. Road or rail silo transport also available..
Additive-free LDPE with increased density
- CAS
- 9002-88-4
- TN-VED Code
- 3901 10
- Category
- Thermoplastic Polymers
Test Methods
ISO 1133-1 · ISO 1183-1 · ISO 527-1,3 · ISO 7765-1 method A · ASTM D1003 · ISO 306/A 50
Key features
Why this product?
- [1] Density: pressed mould specimen per internal method. [2] ISO 294-1 injection moulded specimen. [6] 50 µm blown film; melt 200 °C, blow-up ratio 2.5:1. Observe fire safety rules for combustible materials.
- [1] Density has been measured on pressed mould specimen according to internal method.
- [2] Typical properties measured on standard injection moulded test specimen according to ISO 294-1.
- [6] Film properties tested using 50 µm thick blown film extruded at melt temperature of 200°C and blow up ratio 2.5:1.
- Applications are recommendations, not guarantees; users must test suitability and final-article regulatory compliance, including food contact.
- Heat-treated PRS pooled pallets are collected after use for reuse and remain the pallet provider’s property at all times.
- Additive-free film grade of low density polyethylene with increased density (MD LDPE), characterized by high rigidity, good optical properties and chemical resistance.
- The producer commits to fully respect legislation and uses only REACH-compliant raw materials.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com