Polietilen PE4BM-50
| Parameter | Value | Test Yöntemi |
|---|---|---|
| Production method | Gas-phase polymerisation using Unipol technology | |
| Processing method | Extrusion, blow moulding | |
| Density (at 23°C), g/cm³ | 0,948 - 0,952 | ASTM D 1505 / ISO 1183 |
| Melt flow index, g/10 min, 190°C/21,6 kgf | 3,6 - 5,6 | ASTM D 1238 / ISO 1133 |
| MFI21,6/MFI5 ratio, min. | min 18 | ASTM D 1238 / ISO 1133 |
| Tensile yield strength, MPa (kgf/cm²), min. | min 23,5 (240) | ASTM D 638 / ISO 527 |
| Tensile strength, MPa (kgf/cm²), min. | min 300 | ASTM D 638 / ISO 527 |
| Elongation at break, %, min. | min 600 | ASTM D 638 / ISO 527 |
| Purity grade, min. | min 90 | |
| Cracking resistance (ESCR), hours, min. | min 500 | ASTM D 1693 |
| Thermostability (210°C), min, min. | min 20 | ASTM D 3895 / ISO 11357-6 |
Containers larger than 200 litres. Food-contact products up to 80°C and medical products.
- Large-Volume Container Manufacturing
- Blow Moulding
- Food Packaging
- Medical Product Manufacturing
- Industrial Plastic Tanks
Polyethylene is packed in 25 kg polyethylene or polypropylene bags and transported by rail and road.
Shelf Life
5 years from the date of manufacture