Recycled PP GF30 Compound 40IHGF30-601
30% glass fiber filled PP (PPGF30)
- MFR (230 °C / 2.16 kg)
- Typical: 13 g/10min
- Density
- Typical: 1,16 g/cm³
- Tensile modulus
- Typical: 7500 MPa
- Tensile stress at yield
- Typical: 85 MPa
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| MFR (230 °C / 2.16 kg) | Typical: 13 g/10min | ISO 1133 · °C |
| Density | Typical: 1,16 g/cm³ | ISO 1183/A · g/cm³ |
| Tensile modulus | Typical: 7500 MPa | ISO 527-1,2 |
| Tensile stress at yield | Typical: 85 MPa | ISO 527-1,2 |
| Tensile strain at break | Typical: 4 % | ISO 527-1,2 · % |
| Charpy impact resistance (23 °C, notched) | Typical: 10 kJ/m² | ISO 179/1eA · °C |
| HDT (455 kPa) | Typical: 155 °C | ISO 75-1,2 · °C |
Detailed application areas
Injection molding; automotive, household appliances, building and construction, industrial and furniture applications. Shall not be used for medical, pharmaceutical, food or drinking water applications.
Packaging & storage
Storage
Store dry, protected from direct sunlight. Avoid prolonged storage above 50 °C. Improper storage may deteriorate product performance.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
Recycled PP GF30 Compound 40IHGF30-601 is an industrial product in the recycled pp compounds category. Typical specifications: MFR (230 °C / 2.16 kg): Typical: 13 g/10min; Density: Typical: 1,16 g/cm³; Tensile modulus: Typical: 7500 MPa.
30% glass fiber filled PP (PPGF30); 40% post-industrial recyclate (PIR) Developed for injection molding; high stiffness, high tensile strength, long-term heat stability (LTHS) and stability against metals.
- Category
- Recycled PP Compounds
Synonyms
Test Methods
ISO 1133 · ISO 1183/A · ISO 527-1,2 · ISO 179/1eA · ISO 75-1,2
Key features
Why this product?
- TYPICAL PROPERTIES (NOT FOR SPECIFICATION)
- Appearance: Standard black
- Recommended processing temperature on standard injection molding machines: 210–250 °C. Normally no drying is necessary; if wet during transport or storage, pre-drying for about 2 hours at 80 °C is recommended.
- MATERIAL / TEST: Mechanical tests: ISO 294-1 injection molded specimens; conditioned at room temperature for 72 h (ISO 291). Dedicated shredding/cleaning enables recycling; clean in-house production waste can be directly recycled.
- Mechanical property values from several measurements on standard injection molded specimens; typical properties are not to be used as specification.
- Designed for easy processability on standard injection molding machines.