Recycled PP Talc20 Compound 25CCMT20-701
20% talc filled PP (PPTD20)
- MFR (230 °C / 2.16 kg)
- Typical: 16 g/10 min
- Density
- Typical: 1.05 g/cm³
- Tensile modulus
- Typical: 1500 MPa
- Tensile stress at yield
- Typical: 20 MPa
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| MFR (230 °C / 2.16 kg) | Typical: 16 g/10 min | ISO 1133 · °C |
| Density | Typical: 1.05 g/cm³ | ISO 1183/A · g/cm³ |
| Tensile modulus | Typical: 1500 MPa | ISO 527-1,2 |
| Tensile stress at yield | Typical: 20 MPa | ISO 527-1,2 |
| Tensile strain at break | Typical: 35 % | ISO 527-1,2 · % |
| Charpy impact resistance (23 °C, notched) | Typical: 10 kJ/m² | ISO 179/1eA · °C |
| HDT (455 kPa) | Typical: 95 °C | ISO 75-1,2 · °C |
Detailed application areas
Automotive or general applications such as household appliances, building and construction, industrial and furniture. Shall not be used for medical, pharmaceutical, food and drinking water applications.
Packaging & storage
Storage
Store dry, protected from direct sunlight. Avoid prolonged storage above 50 °C. Improper storage may deteriorate product performance.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
Recycled PP Talc20 Compound 25CCMT20-701 is an industrial product in the recycled pp compounds category. Typical specifications: MFR (230 °C / 2.16 kg): Typical: 16 g/10 min; Density: Typical: 1.05 g/cm³; Tensile modulus: Typical: 1500 MPa.
20% talc filled PP (PPTD20); 25% post-consumer recyclate (PCR) 20% talc filled polypropylene compound (PPTD20) with 25% post-consumer recyclate (PCR), developed for injection molding applications. Sustainable solution with excellent impact-stiffness balance and high tensile strength; available in standard black.
- Category
- Recycled PP Compounds
Synonyms
Test Methods
ISO 1133 · ISO 1183/A · ISO 527-1,2 · ISO 179/1eA · ISO 75-1,2
Key features
Why this product?
- TYPICAL PROPERTIES · NOT SPECIFICATION
- Appearance: Standard black
- Designed for easy processability on standard injection molding machines. Recommended processing temperature: 210–250 °C. Normally no drying is necessary; if wet during transport or storage, pre-drying about 2 hours at 80 °C is recommended.
- MATERIAL: Recyclable with dedicated shredding/cleaning procedures; clean in-house production waste can be directly recycled.
- TEST NOTES: Typical values are not specifications. Mechanical values: standard injection molded specimens (ISO 294-1), conditioned 72 hours at room temperature (ISO 291); several measurements.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com