Polyethylene PE3OT-49
Flat Oriented Tape Manufacturing · Flexible Container Manufacturing · Film Production
- Production method
- Gas-phase polymerisation using Unipol technology
- Processing method
- Extrusion, blow moulding
- Density (at 23°C), g/cm³
- 0,950 – 0,955
- Melt flow index, g/10 min, 190°C/5,0 kgf
- 2,0 – 2,6
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Production method | Gas-phase polymerisation using Unipol technology | — |
| Processing method | Extrusion, blow moulding | — |
| Density (at 23°C), g/cm³ | 0,950 – 0,955 | ASTM D 1505 / ISO 1183 · °C |
| Melt flow index, g/10 min, 190°C/5,0 kgf | 2,0 – 2,6 | ASTM D 1238 / ISO 1133 · g/10 min |
| Within-batch MFI deviation, %, max. | ±10 | % |
| Purity grade, min. | min 90 | — |
| Tensile yield strength, MPa (kgf/cm²), min. | min 24,5 (250) | ASTM D 638 / ISO 527 |
| Tensile strength, MPa (kgf/cm²), min. | min 27,4 (280) | ASTM D 638 / ISO 527 |
| Elongation at break, %, min. | min 700 | ASTM D 638 / ISO 527 · % |
| Film appearance test, points, min. | +25 | — |
Detailed application areas
Flat oriented tapes and flexible containers (up to 20 litres); film production; food-contact products up to 80°C.
Use Cases
- Flat Oriented Tape Manufacturing
- Flexible Container Manufacturing
- Film Production
- Food Packaging
- Big Bag Manufacturing
Packaging & storage
Packaging
Polyethylene is packed in 25 kg polyethylene or polypropylene bags and transported by rail and road.
Shelf Life
5 years from the date of manufacture
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
View technical data sheet ↗Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
Regulatory and compliance
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
Polyethylene PE3OT-49 is a grade used in flat oriented tape, flexible containers and film, with a melt flow index of 2.0-2.6 g/10 min (190°C/5.0 kgf) and a density of 0.950-0.955 g/cm³ (23°C). Flat oriented tapes and flexible containers (up to 20 litres); film production; food-contact products up to 80°C. Other stated values: Elongation at break min 700 %; Tensile strength min 27.4 (280) MPa (kgf/cm²); Tensile yield strength min 24.5 (250) MPa (kgf/cm²). Typical specifications: Production method: Gas-phase polymerisation using Unipol technology; Processing method: Extrusion, blow moulding; Density (at 23°C), g/cm³ 0,950–0,955. KORKİMYA supplies Polyethylene PE3OT-49 in Polyethylene is packed in 25 kg polyethylene or polypropylene bags and transported by rail and road.. Shelf life: 5 years from the date of manufacture.
Flat oriented tapes and flexible containers (up to 20 litres); film production; food-contact products up to 80°C.
Polyethylene PE3OT-49 is a grade used in flat oriented tape, flexible containers and film, with a melt flow index of 2.0-2.6 g/10 min (190°C/5.0 kgf) and a density of 0.950-0.955 g/cm³ (23°C). Flat oriented tapes and flexible containers (up to 20 litres); film production; food-contact products up to 80°C. Other stated values: Elongation at break min 700 %; Tensile strength min 27.4 (280) MPa (kgf/cm²); Tensile yield strength min 24.5 (250) MPa (kgf/cm²).
- Category
- Thermoplastic Polymers
Test Methods
ASTM D 1505 / ISO 1183 · ASTM D 1238 / ISO 1133 · ASTM D 638 / ISO 527
Frequently asked questions
Where is PE3OT-49 used and how is it processed?
Polyethylene PE3OT-49 is used in flat oriented tape, flexible containers and film. Stated application: Flat oriented tapes and flexible containers (up to 20 litres); film production; food-contact products up to 80°C. Areas of use: Flat Oriented Tape Manufacturing, Flexible Container Manufacturing, Film Production, Food Packaging, Big Bag Manufacturing. Processing method: Extrusion, blow moulding. Production method: Gas-phase polymerisation using Unipol technology.
What are the melt flow index and density of PE3OT-49?
The melt flow index of PE3OT-49 is 2.0-2.6 g/10 min (190°C/5.0 kgf), tested to ASTM D 1238 / ISO 1133. Its density is 0.950-0.955 g/cm³ (23°C), tested to ASTM D 1505 / ISO 1183. Within-batch MFI deviation max ±10 %.
Which other values are stated for PE3OT-49?
Stated values for PE3OT-49: Purity grade min 90; Tensile yield strength min 24.5 (250) MPa (kgf/cm²); Tensile strength min 27.4 (280) MPa (kgf/cm²); Elongation at break min 700 %; Film appearance test min +25 points. Test methods: ASTM D 638 / ISO 527.