Polyethylene PE4BP-30
Pipe Manufacturing · Fittings Manufacturing · Blow Moulding
- Production method
- Gas-phase polymerisation using Unipol technology
- Processing method
- Extrusion, blow moulding
- Density (at 23°C), g/cm³
- 0,930 – 0,935
- Melt flow index, g/10 min, 190°C/5,0 kgf
- 1,1 – 1,5
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Production method | Gas-phase polymerisation using Unipol technology | — |
| Processing method | Extrusion, blow moulding | — |
| Density (at 23°C), g/cm³ | 0,930 – 0,935 | ASTM D 1505 / ISO 1183 · °C |
| Melt flow index, g/10 min, 190°C/5,0 kgf | 1,1 – 1,5 | ASTM D 1238 / ISO 1133 · g/10 min |
| MFI21,6/MFI5 ratio, min. | min 18 | ASTM D 1238 / ISO 1133 |
| Within-batch MFI deviation, %, max. | ±10 | ASTM D 1238 / ISO 1133 · % |
| Purity grade, min. | min 90 | — |
| Tensile yield strength, MPa (kgf/cm²), min. | min 13,7 (140) | ASTM D 638 / ISO 527 |
| Tensile strength, MPa (kgf/cm²), min. | min 24,5 (250) | ASTM D 638 / ISO 527 |
| Elongation at break, %, min. | min 600 | ASTM D 638 / ISO 527 · % |
| Film appearance test, points, min. | +30 | — |
| Tensile test, min, min. | min 20 | — |
| Cracking resistance (ESCR), hours, min. | min 1000 | ASTM D 1693 |
| Brittleness temperature, °C, max. | max -70 | ASTM D 746 / ISO 974 · °C |
| Thermostability (210°C), min, min. | min 20 | ASTM D 3895 / ISO 11357-6 · °C |
Detailed application areas
General-purpose pipes and fittings; blow-moulded containers up to 20 litres; various films from 15 microns. Corresponds to PE 63 class according to ISO 9080:2003.
Use Cases
- Pipe Manufacturing
- Fittings Manufacturing
- Blow Moulding
- Film Production
- General Polymer Manufacturing
Packaging & storage
Packaging
Polyethylene is packed in 25 kg polyethylene or polypropylene bags and transported by rail and road.
Shelf Life
5 years from the date of manufacture
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
View technical data sheet ↗Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
Regulatory and compliance
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
Polyethylene PE4BP-30 is a grade used in pipes, fittings, blow-moulded containers of up to 20 litres and film, with a melt flow index of 1.1-1.5 g/10 min (190°C/5.0 kgf) and a density of 0.930-0.935 g/cm³ (23°C). General-purpose pipes and fittings; blow-moulded containers up to 20 litres; various films from 15 microns. Corresponds to PE 63 class according to ISO 9080:2003. Other stated values: Cracking resistance (ESCR) min 1000 hours; Brittleness temperature max -70 °C; Thermostability (210°C) min 20 min. Typical specifications: Production method: Gas-phase polymerisation using Unipol technology; Processing method: Extrusion, blow moulding; Density (at 23°C), g/cm³ 0,930–0,935. KORKİMYA supplies Polyethylene PE4BP-30 in Polyethylene is packed in 25 kg polyethylene or polypropylene bags and transported by rail and road.. Shelf life: 5 years from the date of manufacture.
General-purpose pipes and fittings; blow-moulded containers up to 20 litres; various films from 15 microns. Corresponds to PE 63 class according to ISO 9080:2003.
Polyethylene PE4BP-30 is a grade used in pipes, fittings, blow-moulded containers of up to 20 litres and film, with a melt flow index of 1.1-1.5 g/10 min (190°C/5.0 kgf) and a density of 0.930-0.935 g/cm³ (23°C). General-purpose pipes and fittings; blow-moulded containers up to 20 litres; various films from 15 microns. Corresponds to PE 63 class according to ISO 9080:2003. Other stated values: Cracking resistance (ESCR) min 1000 hours; Brittleness temperature max -70 °C; Thermostability (210°C) min 20 min.
- Category
- Thermoplastic Polymers
Test Methods
ASTM D 1505 / ISO 1183 · ASTM D 1238 / ISO 1133 · ASTM D 638 / ISO 527 · ASTM D 1693 · ASTM D 746 / ISO 974 · ASTM D 3895 / ISO 11357-6
Frequently asked questions
Where is PE4BP-30 used and how is it processed?
Polyethylene PE4BP-30 is used in pipes, fittings, blow-moulded containers of up to 20 litres and film. Stated application: General-purpose pipes and fittings; blow-moulded containers up to 20 litres; various films from 15 microns. Corresponds to PE 63 class according to ISO 9080:2003. Areas of use: Pipe Manufacturing, Fittings Manufacturing, Blow Moulding, Film Production, General Polymer Manufacturing. Processing method: Extrusion, blow moulding. Production method: Gas-phase polymerisation using Unipol technology.
What are the melt flow index and density of PE4BP-30?
The melt flow index of PE4BP-30 is 1.1-1.5 g/10 min (190°C/5.0 kgf), tested to ASTM D 1238 / ISO 1133. Its density is 0.930-0.935 g/cm³ (23°C), tested to ASTM D 1505 / ISO 1183. MFI21.6/MFI5 ratio min 18. Within-batch MFI deviation max ±10 %.
Which other values are stated for PE4BP-30?
Stated values for PE4BP-30: Purity grade min 90; Tensile yield strength min 13.7 (140) MPa (kgf/cm²); Tensile strength min 24.5 (250) MPa (kgf/cm²); Elongation at break min 600 %; Film appearance test min +30 points; Tensile test min 20 min; Cracking resistance (ESCR) min 1000 hours; Brittleness temperature max -70 °C; Thermostability (210°C) min 20 min. Test methods: ASTM D 638 / ISO 527; ASTM D 1693; ASTM D 746 / ISO 974; ASTM D 3895 / ISO 11357-6.