PP Homopolymer Injection Grade H 955
CAS 9003-07-0
Generic registry number (not stated in the manufacturer TDS)
Polypropylene homopolymer
- MFR (230 °C, 2.16 kg)
- Typical: 55 g/10 min
- Tensile stress at yield [2]
- Typical: 36 MPa
- Tensile strain at yield [2]
- Typical: 7.5 %
- Flexural modulus [2]
- Typical: 1700 MPa
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Appearance | Pellets | |
| MFR (230 °C, 2.16 kg) | Typical: 55 g/10 min | ISO 1133-1 · °C |
| Tensile stress at yield [2] | Typical: 36 MPa | ISO 527-1,2 |
| Tensile strain at yield [2] | Typical: 7.5 % | ISO 527-1,2 · % |
| Flexural modulus [2] | Typical: 1700 MPa | ISO 178 |
| Izod impact strength (notched, 23 °C) [2] | Typical: 2.5 kJ/m² | ISO 180/A · °C |
| HDT (0.45 MPa, flatwise) [2] | Typical: 81 °C | ISO 75-1,2 · °C |
| OIT (210 °C) | Typical: > 10 min | EN 728 · °C |
| C-emission (120 °C, 5 h) | Typical: < 50 μgC/g | VDA 277 · °C |
| Recommended processing temperature | Typical: 190 – 235 °C | °C |
Detailed application areas
Compounds for automotive interior parts and injection moulding of thin-wall products for packaging. Can be used in conventional extrusion and injection moulding machines. Not intended for medical & pharmaceutical applications.
Packaging & storage
Packaging
25 kg PE bags; 1375 kg polymer on shrink- or stretch-wrapped pallets. Road or rail silo transport is also available.
Storage
Protect from UV radiation and temperatures above 40 °C.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
PP Homopolymer Injection Grade H 955 (CAS 9003-07-0) is an industrial product in the thermoplastic polymers category. Typical specifications: Appearance: Pellets; MFR (230 °C, 2.16 kg): Typical: 55 g/10 min; Tensile stress at yield [2]: Typical: 36 MPa. KORKİMYA supplies PP Homopolymer Injection Grade H 955 in 25 kg PE bags; 1375 kg polymer on shrink- or stretch-wrapped pallets. Road or rail silo transport is also available..
Polypropylene homopolymer
- CAS
- 9003-07-0
- TN-VED Code
- 3902 10
- Category
- Thermoplastic Polymers
Synonyms
Test Methods
ISO 1133-1 · ISO 527-1,2 · ISO 178 · ISO 180/A · ISO 75-1,2 · EN 728 · VDA 277
Key features
Why this product?
- Observe fire safety rules for combustible materials. Lift adhesive-held bags first without rotation. If moisture condenses inside packaging, drying pellets before use is recommended.
- [2] Typical properties measured on standard injection moulded test specimens according to ISO 294-1. Typical values are not to be used as specification.
- High-speed injection: good processability, excellent flow, low C-emission.
- Contains antioxidants/acid scavenger.
- Low odour/VOC/FOG compound potential depends on added materials.
- Automotive interior compounds, thin-wall packaging.
- Conventional extrusion/injection.
- Not intended for medical/pharmaceutical use.
- Combustible; observe fire safety rules.
- Adhesive prevents bag slipping; lift bags first without rotation.
- Drying pellets before use is recommended if high humidity/fluctuating temperatures cause packaging condensation.
- REACH: polymers exempt; monomers/relevant additives registered, raw materials compliant; no specifically identified SVHC >0.1% at source date.
- Suitable for modern recycling; keep in-house production waste clean.
- Product compliance: DDS.
- 25 kg PE bags; shrink/stretch pallet: 1375 kg.
- Road/rail silo also available.
- Heat-treated pooled pallets are collected after use for reuse and remain the pallet provider’s property.
- Newly developed homopolymer polypropylene for high-speed injection molding; excellent flowability, low C-emission and good processability.
- Potential for compounds with low odour, VOC and FOG properties depends on additional materials introduced during processing.
- Contains antioxidants and acid scavenger.
- High humidity and fluctuating temperatures can cause atmospheric moisture to condense inside packaging.
- Adhesive between bags prevents slipping; lift bags first without rotation.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com