HDPE Recycled Blow Molding Grade 50CHDUF00-2D22
Bimodal HDPE
- MFR (190 °C / 2.16 kg)
- Typical: 0.3 g/10 min
- MFR (190 °C / 5 kg)
- Typical: 1.3 g/10 min
- MFR (190 °C / 21.6 kg)
- Typical: 27 g/10 min
- Density
- Typical: 0.955 g/cm³
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| MFR (190 °C / 2.16 kg) | Typical: 0.3 g/10 min | ISO 1133 · °C |
| MFR (190 °C / 5 kg) | Typical: 1.3 g/10 min | ISO 1133 · °C |
| MFR (190 °C / 21.6 kg) | Typical: 27 g/10 min | ISO 1133 · °C |
| Density | Typical: 0.955 g/cm³ | ISO 1183/A · g/cm³ |
| Flexural modulus | Typical: 1300 MPa | ISO 178 |
| Tensile stress at yield | Typical: 25 MPa | ISO 527-1,2 |
| Tensile strain at break (MD/TD) | Typical: 750 % | ISO 527-1,2 · % |
| Izod impact resistance (23 °C, notched) | Typical: 9 kJ/m² | ISO 180/A · °C |
| ESCR F50 B (10% Igepal CO-630) | Typical: 260 h | ASTM D1693 · % |
| OIT – Oxidation Induction Time (200 °C) | Typical: 15 min | EN 728 · °C |
Detailed application areas
Alternative to 6300B; bottles and cans up to 10 litres for non-aggressive household chemicals, cosmetics and oils; non-pressure and corrugated pipes. Must not be used for medical, pharmaceutical, food, drinking water applications or toys.
Packaging & storage
Packaging
Big-bags or 25 kg polyethylene bags on shrink- or stretch-wrapped pallets.
Storage
Protect from UV and temperatures above 40 °C. Dry before use if humidity and temperature fluctuations cause condensation in packaging.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
HDPE Recycled Blow Molding Grade 50CHDUF00-2D22 is an industrial product in the pe compounds category. Typical specifications: MFR (190 °C / 2.16 kg): Typical: 0.3 g/10 min; MFR (190 °C / 5 kg): Typical: 1.3 g/10 min; MFR (190 °C / 21.6 kg): Typical: 27 g/10 min. KORKİMYA supplies HDPE Recycled Blow Molding Grade 50CHDUF00-2D22 in Big-bags or 25 kg polyethylene bags on shrink- or stretch-wrapped pallets..
Bimodal HDPE; 50% post-consumer recyclate Developed for extrusion blow molding; high stiffness and lowered carbon footprint. Special additivation enables repeated recycling.
- Category
- PE Compounds
Synonyms
Test Methods
ISO 1133 · ISO 1183/A · ISO 178 · ISO 527-1,2 · ISO 180/A · ASTM D1693 · EN 728
Key features
Why this product?
- TYPICAL PROPERTIES · NOT SPECIFICATION
- Appearance: Grey or white pellets
- Standard extrusion blow molding machines; recommended temperature 180–220 °C. Drying is normally unnecessary; if wet, pre-dry for about 2 hours at 80 °C. Observe fire safety rules for combustible materials. Bags may have adhesive between them; lift from pallets first without rotation.
- TEST NOTE: Mechanical values: ISO 293 standard compression molded specimens; conditioned at room temperature for 72 hours (ISO 291).
- Designed for easy processability on standard extrusion blow molding machines.