HDPE Recycled Blow Molding Grade 50CHDUF00-2D31
Unimodal HDPE
- MFR (190 °C / 2.16 kg)
- Typical: 0.3 g/10 min
- MFR (190 °C / 5 kg)
- Typical: 1.5 g/10 min
- MFR (190 °C / 21.6 kg)
- Typical: 28 g/10 min
- Density
- Typical: 0.957 g/cm³
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| MFR (190 °C / 2.16 kg) | Typical: 0.3 g/10 min | ISO 1133 · °C |
| MFR (190 °C / 5 kg) | Typical: 1.5 g/10 min | ISO 1133 · °C |
| MFR (190 °C / 21.6 kg) | Typical: 28 g/10 min | ISO 1133 · °C |
| Density | Typical: 0.957 g/cm³ | ISO 1183/A · g/cm³ |
| Flexural modulus | Typical: 1300 MPa | ISO 178 |
| Tensile stress at yield | Typical: 29 MPa | ISO 527-1,2 |
| Tensile strain at break (MD/TD) | Typical: 400 % | ISO 527-1,2 · % |
| Izod impact resistance (23 °C, notched) | Typical: 12 kJ/m² | ISO 180/A · °C |
| ESCR F50 B (100% Igepal CO-630) | Typical: 35 h | ASTM D1693 · % |
| OIT (200 °C) | Typical: 50 min | EN 728 · °C |
| Recommended processing temperature | Typical: 180 – 220 °C | °C |
Detailed application areas
Alternative to BA 550-13; bottles and cans up to 30 litres for non-aggressive household chemicals, cosmetics and oils; non-pressure and corrugated pipes. Shall not be used for medical, pharmaceutical, food, drinking water applications or toys.
Packaging & storage
Packaging
Big-bags or 25 kg PE bags; shrink/stretch-wrapped pallets.
Storage
Protect from UV and >40 °C. Humidity and temperature fluctuations may cause condensation; if it occurs, drying before use is recommended.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
HDPE Recycled Blow Molding Grade 50CHDUF00-2D31 is an industrial product in the pe compounds category. Typical specifications: MFR (190 °C / 2.16 kg): Typical: 0.3 g/10 min; MFR (190 °C / 5 kg): Typical: 1.5 g/10 min; MFR (190 °C / 21.6 kg): Typical: 28 g/10 min. KORKİMYA supplies HDPE Recycled Blow Molding Grade 50CHDUF00-2D31 in Big-bags or 25 kg PE bags; shrink/stretch-wrapped pallets..
Unimodal HDPE; 30% PCR PCR: post-consumer recyclate. Lowered carbon footprint; special additivation makes repeated recycling possible.
- Category
- PE Compounds
Synonyms
Test Methods
ISO 1133 · ISO 1183/A · ISO 178 · ISO 527-1,2 · ISO 180/A · ASTM D1693 · EN 728
Key features
Why this product?
- TYPICAL PROPERTIES · NOT SPECIFICATION
- Appearance: Grey or white pellets
- Suitable for standard extrusion blow molding machines. Drying is normally unnecessary; if wet, pre-dry for about 2 hours at 80 °C. Follow fire safety rules; first lift adhesive-bound bags without rotation.
- MATERIAL / NOTE: Mechanical tests: ISO 293 compression-molded specimens; ISO 291, 72 h conditioning at room temperature.
- Designed for easy processability on standard extrusion blow molding machines.
- Recycling is possible using dedicated shredding/cleaning procedures; clean in-house production waste can be directly recycled.
- Mechanical property values are obtained from several measurements.
- If wet during transport or storage, pre-drying for about 2 hours at 80 °C is recommended.
- Combustible material; observe fire safety rules.
- Adhesive may be used between bags to prevent slipping.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com