HDPE Blow Moulding Grade BA 550-13
Generic registry number (not stated in the manufacturer TDS)
HDPE / 1-hexene copolymer
- MFR (190 °C / 2.16 kg)
- Typical: 0.35 g/10 min
- MFR (190 °C / 5 kg)
- Typical: 1.5 g/10 min
- MFR (190 °C / 21.6 kg)
- Typical: 28 g/10 min
- Density (23 °C)
- Typical: 954 kg/m³
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Appearance | Pellets | |
| MFR (190 °C / 2.16 kg) | Typical: 0.35 g/10 min | ISO 1133-1 · °C |
| MFR (190 °C / 5 kg) | Typical: 1.5 g/10 min | ISO 1133-1 · °C |
| MFR (190 °C / 21.6 kg) | Typical: 28 g/10 min | ISO 1133-1 · °C |
| Density (23 °C) | Typical: 954 kg/m³ | ISO 1183-2 · °C |
| Tensile stress at yield | Typical: 29 MPa | ISO 527-3 |
| Tensile strain at yield | Typical: 11 % | ISO 527-3 · % |
| Tensile stress at break | Typical: 21 MPa | ISO 527-3 |
| Tensile strain at break | Typical: 1200 % | ISO 527-3 · % |
| Flexural modulus | Typical: 1500 MPa | ISO 178 |
| Izod impact strength (notched, 23 °C) | Typical: 15 kJ/m² | ISO 180/A · °C |
| Hardness — Shore D | Typical: 65 | ISO 868 |
| Vicat softening temperature | Typical: 130 °C | ISO 306/A 120 · °C |
| ESCR F50 B (100% Igepal CO-630) | Typical: 40 h | ASTM D1693 · % |
| Oxidation induction time (200 °C) | Typical: >5 min | EN 728 · °C |
| Recommended processing temperature | Typical: 180 – 220 °C | °C |
Detailed application areas
Bottles and cans up to 30 litres for non-aggressive household chemicals, cosmetics and oils; non-pressure and corrugated pipes. Suitability and regulatory compliance require user testing.
Packaging & storage
Packaging
25 kg PE bags; shrink- or stretch-wrapped pallets, 1375 kg polymer.
Storage
Protect from UV radiation and temperatures above 40 °C.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
HDPE Blow Moulding Grade BA 550-13 is an industrial product in the thermoplastic polymers category. Typical specifications: Appearance: Pellets; MFR (190 °C / 2.16 kg): Typical: 0.35 g/10 min; MFR (190 °C / 5 kg): Typical: 1.5 g/10 min. KORKİMYA supplies HDPE Blow Moulding Grade BA 550-13 in 25 kg PE bags; shrink- or stretch-wrapped pallets, 1375 kg polymer..
HDPE / 1-hexene copolymer
- TN-VED Code
- 3901 20
- Category
- Thermoplastic Polymers
Synonyms
Test Methods
ISO 1133-1 · ISO 1183-2 · ISO 527-3 · ISO 178 · ISO 180/A · ISO 868 · ISO 306/A 120 · ASTM D1693 · EN 728
Key features
Why this product?
- Use conventional extrusion machines. Observe combustible-material rules; lift adhesive-secured bags without rotation. Dry pellets if condensation occurs.
- Density, tensile properties, flexural modulus, Izod impact strength, Shore D hardness, Vicat softening temperature and ESCR measured on standard pressed specimens (ISO 293), conditioned at room temperature (ISO 291).
- Blown products needing good chemical resistance/high rigidity: ≤30 L bottles/cans for non-aggressive household chemicals, cosmetics and oils; non-pressure/corrugated pipes.
- Suitability/compliance, including food contact: final-article tests; DDS.
- Combustible-material fire rules; lift adhered bags without rotation.
- [3] ISO 293 pressed specimens, ISO 291 room-temperature conditioning.
- Burning: 13 mm/min, FMVSS302 (1998), horizontal 350×100×3 mm pressed specimens.
- Modern recycling; clean production waste directly.
- REACH: polymer exempt; monomers/relevant additives registered; only compliant raw materials.
- No identified SVHC >0.1% at publication.
- Protect from UV and >40 °C.
- High humidity/fluctuating temperatures may cause condensation in packing; dry pellets if present.
- 25 kg PE bags; shrink/stretch pallet: 1375 kg.
- Heat-treated pooling pallets remain provider property; collected for reuse.
- Producer commits to use only REACH-compliant raw materials.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com