HDPE Film Grade 7500F
Generic registry number (not stated in the manufacturer TDS)
Bimodal HDPE copolymer
- MFR (190 °C, 2.16 kg)
- Typical: 0.095 g/10 min
- MFR (190 °C, 5 kg)
- Typical: 0.3 g/10 min
- MFR (190 °C, 21.6 kg)
- Typical: 10 g/10 min
- Density (23 °C) [3]
- Typical: 952 kg/m³
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Appearance | Pellets | |
| MFR (190 °C, 2.16 kg) | Typical: 0.095 g/10 min | ISO 1133-1 · °C |
| MFR (190 °C, 5 kg) | Typical: 0.3 g/10 min | ISO 1133-1 · °C |
| MFR (190 °C, 21.6 kg) | Typical: 10 g/10 min | ISO 1133-1 · °C |
| Density (23 °C) [3] | Typical: 952 kg/m³ | ISO 1183-2 · °C |
| Tensile stress at yield (MD/TD) [14] | Typical: 26 / 21 MPa | ISO 527-3 |
| Tensile stress at break (MD/TD) [14] | Typical: 60 / 44 MPa | ISO 527-3 |
| Tensile strain at break (MD/TD) [14] | Typical: 500 / 600 % | ISO 527-3 · % |
| Flexural modulus [3] | Typical: 1400 MPa | ISO 178 |
| Notched Izod impact strength (23 °C) [3] | Typical: 16 kJ/m² | ISO 180/A · °C |
| Elmendorf tear resistance (MD/TD) [14] | Typical: 14 / 140 cN | ISO 6383-2 |
| Dart drop [14] | Typical: 180 g | ISO 7765-1 method A |
| Shore D hardness [3] | Typical: 64 | ISO 868 |
| Vicat softening temperature [3] | Typical: 128 °C | ISO 306/A 120 · °C |
| Oxidation induction time (200 °C) | Typical: 55 min | EN 728 · °C |
| Recommended film thickness | Typical: 0.006 – 0.06 mm | |
| Recommended processing temperature | Typical: 180 – 220 °C | °C |
Detailed application areas
Waste and storage bags, ultra-thin films; conventional extrusion. User tests are required for suitability and regulatory compliance.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
HDPE Film Grade 7500F is an industrial product in the thermoplastic polymers category. Typical specifications: Appearance: Pellets; MFR (190 °C, 2.16 kg): Typical: 0.095 g/10 min; MFR (190 °C, 5 kg): Typical: 0.3 g/10 min.
Bimodal HDPE copolymer; butene-1
- TN-VED Code
- 3901 20
- Category
- Thermoplastic Polymers
Test Methods
ISO 1133-1 · ISO 1183-2 · ISO 527-3 · ISO 178 · ISO 180/A · ISO 6383-2 · ISO 7765-1 method A · ISO 868 · ISO 306/A 120 · EN 728
Key features
Why this product?
- Observe combustible-material fire rules. Lift adhesive-held bags without rotation first. Dry pellets before use if condensation occurs.
- Avoid UV and temperatures above 40 °C. 25 kg PE bags; shrink/stretch-wrapped pallets: 1375 kg polymer. Antioxidant/acid scavenger. [3] Pressed specimens ISO 293; room-temperature conditioning ISO 291. [14] Film measurement averages: 0.015 mm, blow-up 4:1; MD/TD machine/transverse direction.
- Blown film: excellent mechanical strength, good stiffness, good high-speed processability.
- Waste/storage bags, ultra-thin film; conventional extrusion.
- User must test suitability and final articles for regulations including food contact.
- Product compliance/safety: DDS.
- Observe warehouse fire rules for combustible materials.
- Bags have anti-slip adhesive: lift first without rotation.
- High humidity/fluctuating temperatures may cause condensation inside packaging; dry pellets before use.
- Avoid UV and >40 °C. 25 kg PE bags; shrink/stretch pallet: 1375 kg polymer.
- PRS heat-treated pooled pallets are collected after use for circular reuse; remain PRS property.
- [3] ISO 293 pressed specimens, ISO 291 room-temperature conditioning.
- [14] Mean film measurements: 0.015 mm, blow-up 4:1; MD/TD machine/transverse direction.
- Polymers exempt from REACH registration; monomers/relevant additives registered; only REACH-compliant raw materials used.
- At document date no identified SVHC exceeds 0.1%.
- Suitable for modern recycling; keep production waste clean for direct recycling.