PP Impact Copolymer Film Grade K 695
CAS 9010-79-1
Generic registry number (not stated in the manufacturer TDS)
High molecular weight impact copolymer polypropylene
- Melt mass-flow rate
- Typical: 2 g/10 min
- Tensile stress at yield
- Typical: 27 MPa
- Tensile strain at yield
- Typical: 7.7 %
- Flexural modulus
- Typical: 1400 MPa
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Melt mass-flow rate | Typical: 2 g/10 min | ISO 1133-1 · g/10 min |
| Tensile stress at yield | Typical: 27 MPa | ISO 527-1,2 |
| Tensile strain at yield | Typical: 7.7 % | ISO 527-1,2 · % |
| Flexural modulus | Typical: 1400 MPa | ISO 178 |
| Izod impact strength (notched, 23 °C) | Typical: 18 kJ/m² | ISO 180/A · °C |
| Izod impact strength (notched, −20 °C) | Typical: 6 kJ/m² | ISO 180/A · °C |
| Film quality | Typical: 0–300 defect/m² | ISO 11357-3 |
| HDT (0.45 MPa, flatwise) | Typical: 97 °C | ISO 75-1,2 · °C |
| Recommended processing temperature | Typical: 190–240 °C | °C |
Detailed application areas
Medium-low weight corrugated cardboards, blow moulded bottles, cast and blown film, thermoforming sheets, heavy-duty packaging and large containers. Not intended for medical or pharmaceutical applications.
Packaging & storage
Packaging
25 kg PE bags; shrink/stretch-wrapped pallets, 1375 kg polymer. Road/rail silo transport also available.
Storage
Protect from UV and temperatures above 40 °C. Drying pellets before use is recommended if condensation occurs.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
PP Impact Copolymer Film Grade K 695 (CAS 9010-79-1) is an industrial product in the thermoplastic polymers category. Typical specifications: Melt mass-flow rate: Typical: 2 g/10 min; Tensile stress at yield: Typical: 27 MPa; Tensile strain at yield: Typical: 7.7 %. KORKİMYA supplies PP Impact Copolymer Film Grade K 695 in 25 kg PE bags; shrink/stretch-wrapped pallets, 1375 kg polymer. Road/rail silo transport also available..
High molecular weight impact copolymer polypropylene
- CAS
- 9010-79-1
- TN-VED Code
- 3902 30
- Category
- Thermoplastic Polymers
Synonyms
Test Methods
ISO 1133-1 · ISO 527-1,2 · ISO 178 · ISO 180/A · ISO 11357-3 · ISO 75-1,2
Key features
Why this product?
- Can be used in conventional extrusion and injection moulding machines. Combustible; observe fire rules. Lift adhered bags without rotation first. [2] Standard injection moulded specimens according to ISO 294-1.
- [2] Typical properties measured on standard injection moulded test specimen according to ISO 294-1.
- High molecular weight PP impact copolymer for blown/cast film extrusion and injection moulding.
- Adhesive between bags prevents slipping.
- Protect from UV and >40 °C.
- High humidity and temperature changes may cause condensation inside packing; dry pellets before use if it occurs.
- Heat-treated pooled pallets are collected after use for reuse and remain PRS property.
- Product compliance: see DDS.
- Polymers are exempt from REACH registration; monomers and relevant additives are registered.
- Producer uses only REACH-compliant raw materials; no specifically identified SVHC >0.1% at source publication.
- Suitable for modern recycling methods; keep production waste clean for direct recycling.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com