HDPE Blow Moulding Grade 7300B
Generic registry number (not stated in the manufacturer TDS)
Bimodal HDPE copolymer
- MFR (190 °C, 2.16 kg)
- Typical: 0.1 g/10 min
- MFR (190 °C, 5 kg)
- Typical: 0.4 g/10 min
- MFR (190 °C, 21.6 kg)
- Typical: 11 g/10 min
- Density (23 °C)
- Typical: 954 kg/m³
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| MFR (190 °C, 2.16 kg) | Typical: 0.1 g/10 min | ISO 1133-1 · °C |
| MFR (190 °C, 5 kg) | Typical: 0.4 g/10 min | ISO 1133-1 · °C |
| MFR (190 °C, 21.6 kg) | Typical: 11 g/10 min | ISO 1133-1 · °C |
| Density (23 °C) | Typical: 954 kg/m³ | ISO 1183-2 · °C |
| Tensile stress at yield | Typical: 28 MPa | ISO 527-3 |
| Tensile strain at yield | Typical: 11 % | ISO 527-3 · % |
| Tensile stress at break | Typical: 30 MPa | ISO 527-3 |
| Tensile strain at break | Typical: 1350 % | ISO 527-3 · % |
| Flexural modulus | Typical: 1500 MPa | ISO 178 |
| Izod impact strength (notched, 23 °C) | Typical: 15 kJ/m² | ISO 180/A · °C |
| Hardness – Shore D | Typical: 65 | ISO 868 |
| Vicat softening temperature | Typical: 129 °C | ISO 306/A 120 · °C |
| ESCR F50 B (10% Igepal CO-630) | Typical: > 800 h | ASTM D1693 · % |
| Oxidation induction time (200 °C) | Typical: 50 min | EN 728 · °C |
| Recommended processing temperature | Typical: 180 – 220 °C | °C |
Detailed application areas
Recommendations, not guarantees: jerry cans for aggressive industrial chemicals subject to UN certificates; sheet extrusion; corrugated pipes. User tests must assess suitability and regulatory compliance.
Packaging & storage
Storage
Avoid UV and temperatures above 40 °C. High humidity/temperature fluctuations may cause condensation.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
HDPE Blow Moulding Grade 7300B is an industrial product in the thermoplastic polymers category. Typical specifications: MFR (190 °C, 2.16 kg): Typical: 0.1 g/10 min; MFR (190 °C, 5 kg): Typical: 0.4 g/10 min; MFR (190 °C, 21.6 kg): Typical: 11 g/10 min.
Bimodal HDPE copolymer; butene-1
- TN-VED Code
- 3901 20
- Category
- Thermoplastic Polymers
Test Methods
ISO 1133-1 · ISO 1183-2 · ISO 527-3 · ISO 178 · ISO 180/A · ISO 868 · ISO 306/A 120 · ASTM D1693 · EN 728
Key features
Why this product?
- Conventional extrusion machines are suitable. Lift bags first without rotation; observe fire rules for combustible materials. Dry pellets if condensation occurs. Density, tensile, flexural, Izod, Shore D, Vicat and ESCR: ISO 293 pressed specimens; ISO 291 room-temperature conditioning.
- 25 kg polyethylene bags; 1375 kg polymer load on shrink- or stretch-wrapped pallets.
- Blow moulding for high stiffness and excellent ESCR.
- User tests assess suitability and regulatory compliance.
- Lift anti-slip adhesive-bound bags without rotation; follow combustible-material fire rules; dry pellets if condensation occurs.
- [3] ISO 293 pressed specimens; ISO 291 room-temperature conditioning.
- Modern recycling suitable; keep production waste clean for direct recycling.
- Compliance/safety: DDS.
- At source date, REACH: polymer registration-exempt; monomers/relevant additives registered; only compliant raw materials; no identified SVHC >0.1%.
- Bimodal HDPE copolymer; butene-1; pellets
- 25 kg PE bags; shrink/stretch pallets, 1375 kg polymer.
- Heat-treated PRS (Faber Halbertma Group) pallets are collected for reuse; remain PRS property.
- Density, tensile, flexural, Izod, Shore D, Vicat and ESCR values: ISO 293 standard pressed specimens conditioned at room temperature per ISO 291.
- Intended for high stiffness and excellent environmental stress crack resistance.
- Suitable for modern recycling methods; keep in-house production waste clean for direct recycling.