HDPE Fiber Grade 5700S
Generic registry number (not stated in the manufacturer TDS)
HDPE copolymer (butene-1)
- MFR (190°C; 2.16 / 5 / 21.6 kg)
- Typical: 0.5 / 1.7 / 25 g/10 min
- Density (23°C) [3]
- Typical: 947 kg/m³
- Yield stress (MD/TD) [14]
- Typical: 23 / 23 MPa
- Break stress (MD/TD) [14]
- Typical: 46 / 45 MPa
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Appearance | Pellets | |
| MFR (190°C; 2.16 / 5 / 21.6 kg) | Typical: 0.5 / 1.7 / 25 g/10 min | ISO 1133-1 · °C |
| Density (23°C) [3] | Typical: 947 kg/m³ | ISO 1183-2 · °C |
| Yield stress (MD/TD) [14] | Typical: 23 / 23 MPa | ISO 527-3 |
| Break stress (MD/TD) [14] | Typical: 46 / 45 MPa | ISO 527-3 |
| Tensile strain at break (MD/TD) [14] | Typical: 750 / 900 % | ISO 527-3 · % |
| Flexural modulus [3] | Typical: 1200 MPa | ISO 178 |
| Notched Izod (23°C) [3] | Typical: 10.5 kJ/m² | ISO 180/A · °C |
| Elmendorf tear (MD/TD) [14] | Typical: 17 / 150 cN | ISO 6383-2 |
| Dart drop [14] | Typical: 47 g | ISO 7765-1 method A |
| Hardness - Shore D [3] | Typical: 62 | ISO 868 |
| Vicat softening temperature [3] | Typical: 126 °C | ISO 306/A 120 · °C |
| OIT (200°C) | Typical: 100 min | EN 728 · °C |
| Recommended thickness: primer film / fibre | Typical: 0.06 - 0.12 / 0.018 - 0.025 mm | |
| Recommended processing temperature | Typical: 180 - 220 °C | °C |
Detailed application areas
Split film and tapes, round bale nets; protective netting in agriculture and building. Suitability must be verified by user tests.
Packaging & storage
Packaging
25 kg PE bags; 1375 kg/pallet
Storage
Avoid UV and >40°C. Pallets are shrink/stretch wrapped.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
HDPE Fiber Grade 5700S is an industrial product in the thermoplastic polymers category. Typical specifications: Appearance: Pellets; MFR (190°C; 2.16 / 5 / 21.6 kg): Typical: 0.5 / 1.7 / 25 g/10 min; Density (23°C) [3]: Typical: 947 kg/m³. KORKİMYA supplies HDPE Fiber Grade 5700S in 25 kg PE bags; 1375 kg/pallet.
HDPE copolymer (butene-1)
- TN-VED Code
- 3901 20
- Category
- Thermoplastic Polymers
Test Methods
ISO 1133-1 · ISO 1183-2 · ISO 527-3 · ISO 178 · ISO 180/A · ISO 6383-2 · ISO 7765-1 method A · ISO 868 · ISO 306/A 120 · EN 728
Key features
Why this product?
- Suitable for conventional extrusion. Observe fire safety rules. Lift bags first without rotation; dry pellets before use if condensation occurs.
- [3] ISO 293; ISO 291 room temperature. [14] 0.015 mm film, blow-up 4:1; MD/TD: machine/transverse direction.
- Values measured on standard pressed specimens (ISO 293) conditioned at room temperature (ISO 291).
- Average mechanical property values of several measurements on film (MD = machine direction, TD = trans direction), thickness 0.015 mm, blow up ratio 4:1.
- Fiber extrusion; medium molecular weight, narrow distribution; high tensile strength/elongation, low fibrillation; antioxidant/acid scavenger.
- Split film, tapes, round bale nets, agricultural/building nets.
- Recommendations, not guarantees.
- User must test suitability and final-article compliance (e.g. food contact).
- Compliance/safety: DDS.
- Conventional extrusion; combustible-material fire rules.
- Anti-slip bag adhesive: lift without rotation first.
- Dry if humidity/temperature changes cause condensation.
- Avoid UV/>40°C.
- REACH: polymers exempt; monomers/relevant additives registered, raw materials compliant.
- At source date, no specifically identified SVHC >0.1%.
- Unimodal HDPE/butene-1 copolymer
- Shrink/stretch-wrapped, heat-treated PRS pool pallets collected/reused; PRS property.
- Modern recycling suitable; keep in-house waste clean for direct recycling.
- [3] ISO 293 pressed specimens, ISO 291 room-temperature conditioning.
- [14] Averages of several measurements: 0.015 mm film, blow-up 4:1; MD/TD: machine/transverse direction.
- Heat-treated pallets supplied by PRS, a member of the Faber Halbertma Group, in a pooling system collecting pallets after use for reuse.
- Pallets remain PRS property at all times.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com