HDPE Blow Moulding Grade 6300B
Generic registry number (not stated in the manufacturer TDS)
Bimodal HDPE
- Melt mass-flow rate (190 °C, 2.16 kg)
- Typical: 0.3 g/10 min
- Melt mass-flow rate (190 °C, 5 kg)
- Typical: 1.3 g/10 min
- Melt mass-flow rate (190 °C, 21.6 kg)
- Typical: 30 g/10 min
- Density (23 °C) (3)
- Typical: 954 kg/m³
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Appearance | Pellets | |
| Melt mass-flow rate (190 °C, 2.16 kg) | Typical: 0.3 g/10 min | ISO 1133-1 · °C |
| Melt mass-flow rate (190 °C, 5 kg) | Typical: 1.3 g/10 min | ISO 1133-1 · °C |
| Melt mass-flow rate (190 °C, 21.6 kg) | Typical: 30 g/10 min | ISO 1133-1 · °C |
| Density (23 °C) (3) | Typical: 954 kg/m³ | ISO 1183-2 · °C |
| Tensile stress at yield (3) | Typical: 28 MPa | ISO 527-3 |
| Tensile strain at yield (3) | Typical: 10 % | ISO 527-3 · % |
| Tensile stress at break (3) | Typical: 20 MPa | ISO 527-3 |
| Tensile strain at break (3) | Typical: 1100 % | ISO 527-3 · % |
| Flexural modulus (3) | Typical: 1500 MPa | ISO 178 |
| Izod impact strength (notched, 23 °C) (3) | Typical: 8.5 kJ/m² | ISO 180/A · °C |
| Hardness – Shore D (3) | Typical: 65 | ISO 868 |
| Vicat softening temperature (3) | Typical: 128 °C | ISO 306/A 120 · °C |
| ESCR F50 B (10% Igepal CO-630) (3) | Typical: 350 h | ASTM D1693 · % |
| OIT (200 °C) | Typical: 30 min | EN 728 · °C |
| Recommended processing temperature | Typical: 180 – 220 °C | °C |
Detailed application areas
Recommended: detergent/household chemical containers (≤10 L), aggressive industrial chemical packaging subject to UN certificates, and corrugated pipes. User suitability and regulatory tests required.
Packaging & storage
Packaging
25 kg PE bags
Storage
Protect from UV radiation and temperatures above 40 °C.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
HDPE Blow Moulding Grade 6300B is an industrial product in the thermoplastic polymers category. Typical specifications: Appearance: Pellets; Melt mass-flow rate (190 °C, 2.16 kg): Typical: 0.3 g/10 min; Melt mass-flow rate (190 °C, 5 kg): Typical: 1.3 g/10 min. KORKİMYA supplies HDPE Blow Moulding Grade 6300B in 25 kg PE bags.
Bimodal HDPE; butene-1 copolymer
- TN-VED Code
- 3901 20
- Category
- Thermoplastic Polymers
Test Methods
ISO 1133-1 · ISO 1183-2 · ISO 527-3 · ISO 178 · ISO 180/A · ISO 868 · ISO 306/A 120 · ASTM D1693 · EN 728
Key features
Why this product?
- Contains antioxidant/acid scavenger; conventional extrusion. Observe fire rules; lift bags without rotation; dry if condensation occurs. (3): ISO 293 pressed specimens, ISO 291 room-temperature conditioning.
- 25 kg PE bags; 1375 kg polymer on shrink/stretch-wrapped pallets.
- Bimodal HDPE, butene-1 copolymer; high stiffness and good ESCR.
- Protect from UV and >40 °C.
- High humidity and fluctuating temperatures may cause condensation in packaging; dry pellets before use.
- 25 kg PE bags; 1375 kg on shrink/stretch-wrapped pallets.
- Anti-slip bag adhesive; lift first without rotation.
- Heat-treated PRS pallets are collected after use and reused; remain PRS property.
- Compliance: see DDS.
- REACH: polymer exempt; monomers/relevant additives registered; only REACH-compliant raw materials used.
- No identified SVHC >0.1% at source date.
- Modern recycling suitable; keep production waste clean for direct recycling.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com