LDPE Film Grade FC 2-18
CAS 9002-88-4
Generic registry number (not stated in the manufacturer TDS)
LDPE with increased density (MD LDPE)
- MFR (190 °C, 2.16 kg)
- Typical: 2 g/10 min
- Density (23 °C) [1]
- Typical: 929 kg/m³
- Tensile stress at break (MD/TD) [7]
- Typical: 24 / 23 MPa
- Tensile strain at break (MD/TD) [7]
- Typical: 620 / 680 %
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| Appearance | Pellets | |
| MFR (190 °C, 2.16 kg) | Typical: 2 g/10 min | ISO 1133-1 · °C |
| Density (23 °C) [1] | Typical: 929 kg/m³ | ISO 1183-1 · °C |
| Tensile stress at break (MD/TD) [7] | Typical: 24 / 23 MPa | ISO 527-1,3 |
| Tensile strain at break (MD/TD) [7] | Typical: 620 / 680 % | ISO 527-1,3 · % |
| Dart drop [7] | Typical: 105 g | ISO 7765-1 method A |
| Haze [7] | Typical: 6 % | ASTM D1003 · % |
| Gloss 20° [7] | Typical: 108 | ASTM D2457 |
| Vicat softening temperature [2] | Typical: 103 °C | ISO 306/A 50 · °C |
| Recommended film thickness | Typical: 0.02 – 0.06 mm | |
| Recommended processing temperature | Typical: 160 – 200 °C | °C |
Detailed application areas
Bags and pouches; lamination, blown, bubble, shrink and surface protection films. Conventional extrusion. Users must test suitability and final article regulatory compliance.
Packaging & storage
Packaging
25 kg PE bags; shrink/stretch-wrapped pallet: 1375 kg. Road/rail silo also available.
Storage
Protect from UV radiation and temperatures above 40 °C.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
LDPE Film Grade FC 2-18 (CAS 9002-88-4) is an industrial product in the thermoplastic polymers category. Typical specifications: Appearance: Pellets; MFR (190 °C, 2.16 kg): Typical: 2 g/10 min; Density (23 °C) [1]: Typical: 929 kg/m³. KORKİMYA supplies LDPE Film Grade FC 2-18 in 25 kg PE bags; shrink/stretch-wrapped pallet: 1375 kg. Road/rail silo also available..
LDPE with increased density (MD LDPE)
- CAS
- 9002-88-4
- TN-VED Code
- 3901 10
- Category
- Thermoplastic Polymers
Synonyms
Test Methods
ISO 1133-1 · ISO 1183-1 · ISO 527-1,3 · ISO 7765-1 method A · ASTM D1003 · ASTM D2457 · ISO 306/A 50
Key features
Why this product?
- Observe combustible-material fire safety rules. Drying pellets before use is recommended if humidity and fluctuating temperatures cause condensation in packaging.
- Additives free. [1] Pressed specimen, internal method. [2] ISO 294-1 injection specimen. [7] 50 µm blown film, melt 180 °C; blow-up ratio 2.5:1.
- Applications are recommendations; users must test suitability and final article compliance, including food contact where relevant.
- Films: high rigidity, excellent optical properties, low gel content; very good draw-down and high output when properly fabricated.
- Polymers exempt from REACH registration; monomers and relevant additives registered.
- Producer commits to only REACH-compliant raw materials.
- As of August 2025, no specifically identified SVHC >0.1%.
- Compliance/safety: DDS.
- LDPE with increased density (MD LDPE); additives free.
- Polyethylene resins suitable for modern recycling methods; keep in-house production waste clean to facilitate direct recycling.
- Heat-treated pooling pallets are collected for reuse; remain provider property.
- Film grade of low density polyethylene with increased density (MD LDPE).
- Films have high rigidity, excellent optical properties and low gel content; very good draw down ability with high output when properly fabricated.
- Density measured on pressed mould specimen according to internal method.
- Typical properties measured on standard injection moulded test specimen according to ISO 294-1.
- Film properties tested using 50 µm thick blown film extruded at melt temperature of 180°C and blow up ratio 2.5:1.
- See DDS.
- See MSDS.
- Heat-treated pooling pallets are collected after use for reuse and remain property of the pallet provider.
- Applications are recommendations, not guarantees; users must test suitability and final article compliance, including food contact where relevant.
- See DDS for further product safety information.
Related Products
Last updated: 11/10/2026
MSDS Available · Export Registered · korkimya.com