HDPE Recycled Blow Molding Grade 30CHDUF00-2D32
Unimodal HDPE
- MFR (190 °C, 2.16 kg)
- Typical: 0.3 g/10 min
- MFR (190 °C, 5 kg)
- Typical: 1.4 g/10 min
- MFR (190 °C, 21.6 kg)
- Typical: 28 g/10 min
- Density
- Typical: 0.956 g/cm³
Technical Specifications
| Parameter | Value | Method / unit |
|---|---|---|
| MFR (190 °C, 2.16 kg) | Typical: 0.3 g/10 min | ISO 1133 · °C |
| MFR (190 °C, 5 kg) | Typical: 1.4 g/10 min | ISO 1133 · °C |
| MFR (190 °C, 21.6 kg) | Typical: 28 g/10 min | ISO 1133 · °C |
| Density | Typical: 0.956 g/cm³ | ISO 1183/A · g/cm³ |
| Flexural modulus | Typical: 1350 MPa | ISO 178 |
| Tensile stress at yield | Typical: 29 MPa | ISO 527-1,2 |
| Tensile strain at break (MD/TD) | Typical: 700 % | ISO 527-1,2 · % |
| Izod impact (23 °C, notched) | Typical: 18 kJ/m² | ISO 180/A · °C |
| ESCR F50 B (100% Igepal CO-630) | Typical: 50 h | ASTM D1693 · % |
| Oxidation induction time (200 °C) | Typical: 50 min | EN 728 · °C |
Detailed application areas
Extrusion blow molding: bottles and cans up to 30 liters for non-aggressive household chemicals, cosmetics and oils; non-pressure and corrugated pipes. Shall not be used for medical, pharmaceutical, food, drinking water applications or toys.
Packaging & storage
Packaging
Big-bags or 25 kg PE bags; shrink/stretch-wrapped pallets.
Storage
Protect from UV and >40 °C. Dry before use if condensation occurs in high humidity/fluctuating temperatures.
Documents
Technical data sheet (TDS)
Review the recorded specifications, packaging and storage information.
Safety & lot documents
Request the current SDS and the certificate of analysis (CoA) for the lot you are evaluating.
KORKİMYA supply assurance
Stock in Türkiye
Current availability is confirmed by product and lot with your quote.
KKDİK registered
Every catalog product is KKDİK registered for Türkiye.
CoA for every lot
Verify technical values against the lot's certificate of analysis.
TL invoicing
Turkish lira invoicing is available for domestic purchases.
Payment terms
Discuss terms for your quantity and supply plan when requesting a quote.
Request Sample
Product Information
HDPE Recycled Blow Molding Grade 30CHDUF00-2D32 is an industrial product in the pe compounds category. Typical specifications: MFR (190 °C, 2.16 kg): Typical: 0.3 g/10 min; MFR (190 °C, 5 kg): Typical: 1.4 g/10 min; MFR (190 °C, 21.6 kg): Typical: 28 g/10 min. KORKİMYA supplies HDPE Recycled Blow Molding Grade 30CHDUF00-2D32 in Big-bags or 25 kg PE bags; shrink/stretch-wrapped pallets..
Unimodal HDPE; 30% PCR Unimodal HDPE blend with 30% post-consumer recyclate (PCR), developed for extrusion blow molding; lowered carbon footprint and high ESCR. Special additivation enables repeated recycling. Available in grey and white.
- Category
- PE Compounds
Synonyms
Test Methods
ISO 1133 · ISO 1183/A · ISO 178 · ISO 527-1,2 · ISO 180/A · ASTM D1693 · EN 728
Key features
Why this product?
- TYPICAL PROPERTIES · NOT SPECIFICATIONS
- Appearance: Grey or white pellets
- Processing: 180–220 °C. Drying normally unnecessary; if wet, pre-dry for about 2 hours at 80 °C. Combustible; observe fire rules. Lift adhered bags first without rotation.
- TEST SPECIMENS: Mechanical values: ISO 293 compression molded specimens; ISO 291, 72 hours at room temperature; several measurements.